The T15K6 Alloy with complex coating for increasing durability of tools
DOI:
https://doi.org/10.15407/mom2019.02.026Keywords:
hard alloy, borіding, boron carbide, copper, structure, diffusion, friction, microhardness, wear resistanceAbstract
The results of studies on the application of complex boron coating powder method on hard alloys. Defined phase and chemical composition, thickness and microhardness of the coating on alloys. It was established that after diffusion saturation of hard alloy in boron mixture for 4 hours formed coating with boride phases TiB, WB, CoB and WC, TiC, whose thickness is 30 microns. At complex saturation with boron and copper for 4 hours diffusion saturation formed coating with boride phases TiB, WB, CoB and WC, TiC and separate inclusions of copper with a thickness of the diffusion layer up to 20 microns. Boriding and complex saturation with boron and copper allows in 2 – 2.5 times increase the microhardness of the surface layers of hard alloys, that in turn leads to increased wear resistance.
References
Bogoduhov S.I., Kilov A.S., Shein E.A., Yasakov A.S., Haybullin R.R., Vestnik Orenburgskogo gosudarstvennogo universiteta, 2011, No 5 (124), pp. 164-170 [in Russian].
Zelenkevich O.A., Taran N.G., Lazarev G.E., Kudryavtseva B.M., Himicheskoe i neftyanoe mashinostroenie, 1990, No 4, pp. 28-30 [in Russian].
Klinskaya-Rudenskaya N.A., Kopyisov V.A., Fizika i himiya obrabotki materialov, 1995, No 3, pp. 63-68 [in Russian].
Moiseenko O.I., Chkalova O.N. Instrumentalnyie materialyi (Tool materials), Kiev: Vischa shkola, 1982, 196 p. [in Russian].
Berzina I.G., Gusev E.B., Zakharov B.V., Fedina G.N., Fedin V.M., Fizika metallov i metallovedeniye, 1984, Vol. 57, Issue 4, pp. 713-718 [in Russian].
Zakhariev Z., Petrov K., Christov M., J. Less-Common Metals, 1981, 82, pp. 57-62 [in English].
https://doi.org/10.1016/0022-5088(81)90197-1
Cherneha S.M., Polyakov I. A., Krasovskyy M.A., Lutskyy natsionalnyy tekhnichnyy universytet «Naukovi notatky», 2015, Issue 49, рр. 165-171 [in Ukrainian].
Downloads
Published
Issue
Section
License
Copyright (c) 2019 C.M. Chernega, K.M. Grinenko, I.A. Polyakov
This work is licensed under a Creative Commons Attribution 4.0 International License.